Description
XC-6002C is the polyester polyol component of the XC-6002C / XC-8280 polyester-polyurethane footwear system. This system is designed for double-density safety shoes and casual shoes, with high strength, good abrasion resistance, and oil resistance.
The system can be processed to produce both outsole and midsole components with different density and hardness characteristics, making it suitable for footwear requiring a combination of performance and durability.
Specifications
| Specification | XC-6002C |
|---|---|
| Product Type | Polyester Polyol |
| Appearance | Cream-white liquid |
| Viscosity @ 40°C | 800–1,100 mPa·s |
| Density @ 40°C | 1.01–1.02 g/cm³ |
| Package | 225 kg |
| System | XC-6002C / XC-8280 |
| Application | Double-density safety shoes, casual shoes |
Features
- High-strength footwear PU system
- Good abrasion resistance
- Good oil resistance
- Suitable for safety footwear
- Suitable for casual footwear
- Designed for double-density sole construction
- Suitable for outsole and midsole applications
System Comparison
| Property | XC-2088B / XC-6230T | XC-6002C / XC-8280 |
|---|---|---|
| System focus | Lightweight footwear | Strength & durability |
| TDS characteristic | Good handle, low density, good dimensional stability | High strength, abrasion resistance, oil resistance |
| Main application | Middle sole, insole | Double-density safety shoes, casual shoes |
| Free-rise foam density | 0.20–0.22 g/cm³ | 0.45–0.55 g/cm³ |
| Molded midsole density | 0.38–0.40 g/cm³ | 0.45–0.55 g/cm³ |
| Molded outsole density | Not specified | 0.90–1.10 g/cm³ |
| Hardness | Shore A 30–50 | Outsole: 55–60; Insole: 45–55 |
| Tensile strength | 4.0–5.5 MPa | Outsole: 9.0–11.0 MPa; Insole: 5.0–9.0 MPa |
| Elongation | 300–400% | Not specified |
| Tear/peel strength | Tear: 15–23 kN/m | Peel: 80–100 / 30–45 kN/m |
| Flexing | 40,000 cycles, no crack | 30,000 cycles, no crack |
| Primary selling point | Lightweight/low-density soles | Strong, durable, oil- and abrasion-resistant soles |
Reviews